- Title
- In situ neutron diffraction study of a liquid nitrogen-quenched Mg-PSZ under load: a microcrack-dominated system?
- Creator
- Ma, Yuxiang; Kisi, Erich Herold
- Relation
- Journal of the American Ceramic Society Vol. 88, no. 9, p. 2510-2514
- Publisher
- American Ceramic Society
- Resource Type
- journal article
- Date
- 2005
- Description
- The mechanical response of liquid nitrogen-quenched 9.4 Mg-PSZ in which the orthorhombic (o) phase is the major constituent (46 wt%) was investigated using in-situ neutron diffraction during uniaxial compression. The material remains elastic below 1 GPa with a Young's modulus of~242 GPa, second highest of all zirconia-based materials and highest of all zirconia-based ceramics. Beyond 1 GPa, the material develops small plastic strains in a time-dependent manner (i.e., by room temperature creep) although the strains were generally much smaller than the unquenched material, which contains no o phase. As for standard Mg-PSZ, the creep was accompanied by a volume change usually indicative of tetragonal to monoclinic (m) phase transformation; however, the amount of m phase apparent in the neutron diffraction patterns increased only marginally. The magnitude of the volume increase could not be accounted for by the observed increase in the m phase and hence, microcracking is believed to be responsible for most of the volume change. There is some evidence for a small amount of o to m transformation at the detection limit of the phase analysis technique.
- Identifier
- uon:368
- Identifier
- http://hdl.handle.net/1959.13/25393
- Identifier
- ISSN:1551-2916
- Language
- eng
- Reviewed
- Hits: 969
- Visitors: 904
- Downloads: 0
Thumbnail | File | Description | Size | Format |
---|